Alloy C-4 kemikali idapọ:

Alloy	%	Ni	Cr	Mo	Fe	C	Mn	Si	Co	S	P	Ti
C-4	Min.	65	14	14
O pọju.		18	17	3.0	0.01	1.0	0.08	2.0	0.010	0.025	0.70

 

iwuwo	8,64 g / cm3
Ojuami yo	1350-1400 ℃

 

Alloy	Agbara fifẹ Rm N/mm2	Agbara ikore RP0.2N / mm2	Ilọsiwaju A5%
C-4	783	365	55

Alloy C-4 alloy jẹ nickel-chromium-molybdenum alloy pẹlu dayato si
iduroṣinṣin iwọn otutu ti o ga bi a ti jẹri nipasẹ ductility giga ati ipata ipata paapaa
lẹhin ti ogbo ni iwọn 1200 si 1900 F (649 si 1038 C). Eleyi alloy koju awọn Ibiyi
ti ọkà-aala precipitates ni weld ooru-fowo agbegbe aago, bayi ṣiṣe awọn ti o dara
fun julọ kemikali ilana elo ni bi-welded majemu. C-4 alloy tun
ni o ni o tayọ resistance si wahala-ibajẹ wo inu ati lati oxidizing bugbamu to
1900 F (1038 C).

 

Alloy C-4 alloy ni o ni exceptional resistance si jakejado orisirisi ti kemikali ilana
awọn agbegbe. Iwọnyi pẹlu awọn acid ti o wa ni erupe ile ti a ti doti gbona, awọn nkanmimu, chlorine
ati chlorine ti a ti doti media (Organic ati inorganic), chlorine gbẹ, formic ati
acetic acids, acetic anhydride, ati omi okun ati awọn ojutu brine.
Alloy C-4 alloy le ti wa ni eke, gbona-binu, ati ikolu extruded. Biotilejepe awọn
alloy duro lati ṣiṣẹ-lile, o le ni ifijišẹ jin-kale, yiri, tẹ akoso tabi
punched. Gbogbo awọn ọna ti o wọpọ ti alurinmorin le ṣee lo lati weld Alloy C-4
alloy, biotilejepe oxy-acetylene ati awọn ilana arc submerged ko ṣe iṣeduro
nigbati ohun kan ti a ṣelọpọ ti pinnu fun lilo ninu iṣẹ ipata. Awọn iṣọra pataki
yẹ ki o wa ni ya lati yago fun nmu ooru input.