EN 10088-1 BO'YICHA KIMYO SANOATI UCHUN IKKI FAZALI TUZILMAGA BO'LGAN zanglamaydigan SUPER DUPLEKS STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 SINFI F61.
| Standart | Chelik darajasi | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Kimyoviy tarkibi % | ||||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Mo: | Ni: | Cu: | N: | |
| EN | 1.4507 - X2CrNiMoCuN25-6-3 | |||||||||
| <0,03 | <2,0 | <0,7 | <0,035 | <0,015 | 24,0 - 26,0 | 3,0 – 4,0 | 6,0 – 8,0 | 1,0 – 2,5 | 0,20 - 0,30 | |
| ASTM | UNS S32550 - A182 darajasi F61 - 255 turi | |||||||||
| <0,04 | <1,5 | <1,0 | <0,040 | <0,030 | 24,0 - 27,0 | 2,9 – 3,9 | 4,5 – 6,5 | 1,5 - 2,5 | 0,10 - 0,25 | |
| ASTM | UNS S32520 - A182 darajasi F59 | |||||||||
| <0,03 | <1,5 | <0,8 | <0,035 | <0,020 | 24,0 - 26,0 | 3,0 – 5,0 | 5,5 – 8,0 | 0,5 – 3,0 | 0,20 - 0,35 | |
| JIS | SUS329J4L - SUS 329J4L | |||||||||
| <0,03 | <1,5 | <1,0 | <0,040 | <0,030 | 24,0 - 26,0 | 2,5 - 3,5 | 5,5 – 7,5 | - | 0,08 - 0,30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, F61 darajasi - spetsifikatsiya va dastur
1.4410 / X2CrNiMoN25-7-4 / UNS S32750 ga o'xshash o'ta kuchli kislotaga chidamli zanglamaydigan po'latlar guruhidan maxsus nav. Po'lat korroziyaning har xil turlariga, shu jumladan intergranulyar korroziyaga nisbatan yuqori qarshilikka ega bo'lgan yuqori mustahkamlik xususiyatlarini namoyish etadi. 1.4507 va UNS S32550 materiallari qog'oz, kimyo, azot va aviatsiya sanoatida, shuningdek, energetikada vintlar, vallar, gilzalar, armatura, o'rnatish va quvurlar, nasos qismlari, kimyoviy moddalar uchun tanklar, issiqlik almashtirgichlar, radiator qismlari va boshqalar uchun ishlatiladi. samolyot konstruksiyalari.
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 - mexanik xususiyatlar
- Kuchlanish kuchi, Rm: 700 – 900 MPa
- Chiqish nuqtasi, Rp0,2: >500 MPa
- Cho'zilish, A:> 25%
- Elastiklik moduli, E: 200 GPa
- Qattiqlik, HB: <270
- Issiqlik quvvati, cp: 500 J * kg-1 * K-1
- Issiqlik o'tkazuvchanligi, l: 15 Vt * m-1 * K-1
- Chiziqli kengayish koeffitsienti, a: 13,0 * 10-6 K-1
- Maxsus qarshilik, Ō: 0,8 mkOhm * m
Yuqori haroratda mexanik xususiyatlar - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Harorat (℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Chiziqli kengayish koeffitsienti, a (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Elastiklik moduli, E (GPa) | 194 | - | 186 | - | 180 | |||
| Chiqish nuqtasi, Rp0,2 (MPa) | >450 | >420 | >400 | >380 | - | |||
Issiqlik va plastik ishlov berish 1.4507, UNS S32550
- 1020 - 1100 ℃ da o'ta to'yinganlik
- 1200 - 900 ℃ haroratda prokat va zarb qilish
Etkazib berish vaqti: 23-mart-2020-yil