STAINLESS SUPER DUPLEX STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 DARAJA F61 YENYE MUUNDO WA AWAMU MBILI KWA SEKTA YA KIKEMIKALI KULINGANA NA EN 10088-1.
| Kawaida | Daraja la chuma | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Muundo wa Kemikali % | ||||||||||
| C: | Mh: | Si: | P: | S: | Cr: | Mo: | Ni: | Cu: | N: | |
| EN | 1.4507 - X2CrNiMoCuN25-6-3 | |||||||||
| <0.03 | <2.0 | <0.7 | <0.035 | <0.015 | 24.0 - 26.0 | 3.0 - 4.0 | 6.0 - 8.0 | 1.0 - 2.5 | 0.20 - 0.30 | |
| ASTM | UNS S32550 – A182 daraja F61 – Aina 255 | |||||||||
| <0.04 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 - 27.0 | 2.9 - 3.9 | 4.5 - 6.5 | 1.5 - 2.5 | 0.10 - 0.25 | |
| ASTM | UNS S32520 – A182 daraja F59 | |||||||||
| <0.03 | <1.5 | <0.8 | <0.035 | <0.020 | 24.0 - 26.0 | 3.0 - 5.0 | 5.5 - 8.0 | 0.5 - 3.0 | 0.20 - 0.35 | |
| JIS | SUS329J4L – SUS 329J4L | |||||||||
| <0.03 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 - 26.0 | 2.5 - 3.5 | 5.5 - 7.5 | - | 0.08 - 0.30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, Daraja F61 - vipimo na matumizi
Daraja maalum kutoka kwa kundi la vyuma vya pua vinavyostahimili asidi kali zaidi sawa na 1.4410 / X2CrNiMoN25-7-4 / UNS S32750. Chuma huonyesha mali ya nguvu ya juu na upinzani wa juu kwa aina mbalimbali za kutu, ikiwa ni pamoja na kutu ya intergranular. Nyenzo za 1.4507 na UNS S32550 hutumika katika tasnia ya karatasi, kemikali, nitrojeni, na anga na vile vile katika uhandisi wa nguvu wa screws, shafts, sleeves, fittings, mitambo na mabomba, sehemu za pampu, tanki za kemikali, vibadilisha joto, sehemu za radiator na ujenzi wa ndege.
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 - sifa za mitambo
- Nguvu ya mkazo, Rm: 700 - 900 MPa
- Kiwango cha mavuno, Rp0,2:>500 MPa
- Kurefusha, A:> 25%
- Modulus ya elasticity, E: 200 GPa
- Ugumu, HB: <270
- Uwezo wa joto, cp: 500 J * kg-1 * K-1
- Conductivity ya joto, λ: 15 W * m-1 * K-1
- Mgawo wa upanuzi wa mstari, α: 13.0 * 10-6 K-1
- Upinzani maalum, Ω: 0.8 mkOhm * m
Tabia za mitambo kwa joto la juu - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Halijoto (℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Mgawo wa upanuzi wa mstari, α (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Modulus ya elasticity, E (GPa) | 194 | - | 186 | - | 180 | |||
| Kiwango cha mavuno, Rp0,2 (MPa) | > 450 | > 420 | > 400 | >380 | - | |||
Matibabu ya joto na plastiki 1.4507, UNS S32550
- Kueneza zaidi kwa 1020 - 1100 ℃
- Rolling na forging kwa joto la 1200 - 900 ℃
Muda wa posta: Mar-23-2020