Imeteuliwa kama UNS N08020, Aloi 20 (pia inajulikana kama "Incoloy 020" au "Incoloy 20") ni aloi ya nikeli-iron-chromium yenye nyongeza za shaba na molybdenum. Ina upinzani wa kipekee wa kutu dhidi ya asidi ya sulfuriki, kupasuka kwa mkazo wa kloridi, asidi ya nitriki na asidi ya fosforasi. Aloi 20 inaweza kutengenezwa kwa urahisi au baridi kwa valves, fittings bomba, flanges, fasteners, pampu, mizinga, pamoja na vipengele exchanger joto. Joto la kutengeneza joto linapaswa kuwa kati ya 1400-2150°F [760-1175°C]. Kawaida, matibabu ya joto ya annealing inapaswa kufanywa kwa kiwango cha joto cha 1800-1850 ° F [982-1010 ° C]. Aloi 20 inatumika sana kwa utengenezaji wa petroli, kemikali za kikaboni na isokaboni, usindikaji wa dawa, na tasnia ya chakula.
1. Mahitaji ya Muundo wa Kemikali
| Muundo wa Kemikali wa Aloi 20,% | |
|---|---|
| Nickel | 32.0-38.0 |
| Chromiun | 19.0-21.0 |
| Shaba | 3.0-4.0 |
| Molybdenum | 2.0-3.0 |
| Chuma | Mizani |
| Kaboni | ≤0.07 |
| Niobium+tantalum | 8*C-1.0 |
| Managanese | ≤2.00 |
| Fosforasi | ≤0.045 |
| Sulfuri | ≤0.035 |
| Silikoni | ≤1.00 |
2. Sifa za Mitambo za Aloi 20
ASTM B462 Aloi 20 (UNS N08020) fittings ghushi na flanges ghushi.
| Nguvu ya Mkazo, min. | Nguvu ya Mazao, min. | Kurefusha, min. | Modulus ya Vijana | |||
|---|---|---|---|---|---|---|
| Mpa | ksi | Mpa | ksi | % | 103ksi | Gpa |
| 620 | 90 | 300 | 45 | 40 | 28 | 193 |
3. Sifa za Kimwili za Aloi 20
| Msongamano | Joto Maalum | Upinzani wa Umeme | Uendeshaji wa joto |
|---|---|---|---|
| g/cm3 | J/kg.°C | µΩ·m | W/m.°C |
| 8.08 | 500 | 1.08 | 12.3 |
4. Fomu za Bidhaa na Viwango
| Fomu ya Bidhaa | Kawaida |
|---|---|
| Fimbo, bar na waya | ASTM B473, B472, B462 |
| Sahani, karatasi na strip | ASTM A240, A480, B463, B906 |
| Bomba na bomba isiyo imefumwa | ASTM B729, B829 |
| Bomba la svetsade | ASTM B464, B775 |
| Bomba la svetsade | ASTM B468, B751 |
| Fittings svetsade | ASTM B366 |
| Flanges za kughushi na fittings za kughushi | ASTM B462, B472 |
Muda wa kutuma: Oct-23-2020