STAINLESS SUPER DUPLEX STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 kelas F61 kalawan struktur dua-fase pikeun industri kimia nurutkeun en 10088-1.
| Standar | Kelas Baja | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Komposisi Kimia% | ||||||||||
| C: | Bungbulang: | Si: | P: | S: | Cr: | Mo: | Ni: | Cu: | N: | |
| EN | 1.4507 - X2CrNiMoCuN25-6-3 | |||||||||
| <0.03 | <2.0 | <0.7 | <0,035 | <0,015 | 24.0 – 26.0 | 3.0 – 4.0 | 6.0 – 8.0 | 1.0 – 2.5 | 0.20 – 0.30 | |
| ASTM | UNS S32550 - A182 kelas F61 - Tipe 255 | |||||||||
| <0.04 | <1.5 | <1.0 | <0,040 | <0.030 | 24.0 – 27.0 | 2.9 – 3.9 | 4.5 – 6.5 | 1.5 – 2.5 | 0.10 – 0.25 | |
| ASTM | UNS S32520 - A182 kelas F59 | |||||||||
| <0.03 | <1.5 | <0.8 | <0,035 | <0,020 | 24.0 – 26.0 | 3.0 – 5.0 | 5.5 – 8.0 | 0.5 – 3.0 | 0.20 – 0.35 | |
| JIS | SUS329J4L - SUS 329J4L | |||||||||
| <0.03 | <1.5 | <1.0 | <0,040 | <0.030 | 24.0 – 26.0 | 2.5 – 3.5 | 5.5 – 7.5 | - | 0.08 – 0.30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, Kelas F61 - spésifikasi sareng aplikasi
Kelas husus ti grup baja tahan karat asam super-kuat sarupa 1.4410 / X2CrNiMoN25-7-4 / UNS S32750. Baja nunjukkeun sipat kakuatan anu luhur sareng résistansi anu rélatif luhur pikeun sababaraha jinis korosi, kalebet korosi intergranular. 1.4507 sareng bahan UNS S32550 dianggo dina industri kertas, kimia, nitrogén, sareng penerbangan ogé dina rékayasa listrik pikeun screws, shafts, sleeves, fittings, pamasangan sareng pipelines, bagian pompa, tank pikeun bahan kimia, penukar panas, bagian radiator sareng konstruksi pesawat.
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 - sipat mékanis
- Kakuatan tegangan, Rm: 700 – 900 MPa
- Titik hasil, Rp0,2: >500 MPa
- Elongation, A:> 25%
- Modulus élastisitas, E: 200 GPa
- Teu karasa, HB: <270
- Kapasitas termal, cp: 500 J * kg-1 * K-1
- Konduktivitas termal, λ: 15 W * m-1 * K-1
- Koéfisién ékspansi linier, α: 13,0 * 10-6 K-1
- Résistansi spésifik, Ω: 0,8 mkOhm * m
Sipat mékanis dina suhu luhur - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Suhu (℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Koéfisién ékspansi linier, α (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Modulus élastisitas, E (GPa) | 194 | - | 186 | - | 180 | |||
| Titik hasil, Rp0,2 (MPa) | >450 | >420 | > 400 | >380 | - | |||
Panas jeung perlakuan plastik 1.4507, UNS S32550
- Supersaturation dina 1020 - 1100 ℃
- Rolling jeung forging dina suhu 1200 – 900 ℃
waktos pos: Mar-23-2020