Alloy	%	Ni	Cr	Mo	Cu	N	C	Mn	Si	P	S
254 SMO	Min.	17.5	19.5	6	0.5	0.18
Max.	18.5	20.5	6.5	1	0.22	0.02	1	0.8	0.03	0.01

254SMO Thepa ea 'mele:

Botenya	8.0 g/cm3
Sebaka se qhibilihang	1320-1390 ℃

254SMO bonyane ba thepa ea mochini mocheso oa kamore:

Boemo	Matla a tšepe Rm N Rm N/mm2	Ho hlahisa matla RP0.2N/mm2	Elongation A5 %
254 SMO	650	300	35

 

Sebopeho:
Metsoako e phahameng ea molybdenum, chromium le nitrogen e entsoeng 254SMO e na le khanyetso e ntle haholo ea ts'ebetso ea likoti le maphao. Koporo e ntlafalitse ho thibela kutu ho tse ling tsa asiti. Ho feta moo, ka lebaka la litaba tsa eona tse phahameng tsa nickel, chromium le molybdenum, e le hore 254SMO e be le khatello e ntle ea khatello ea maikutlo.
1.Tlhahiso e ngata e fapaneng ea tšebeliso ea phihlelo e bontšitse hore esita le mocheso oa iin o phahameng, 254SMO metsing a leoatle e boetse e hanyetsana haholo le lekhalo la ts'ebetso ea kutu, ke mefuta e seng mekae feela ea tšepe e sa hloekang e nang le ts'ebetso ena.
2.254SMO e kang pampiri ea bleach e hlokehang bakeng sa tlhahiso ea tharollo ea acidic le tharollo ea halide oxidative corrosion resistance le ho hanyetsa ha kutu e ka bapisoa le e tsitsitseng ka ho fetisisa setsing sa motheo sa nickel le li-alloys tsa titanium.
3.254SMO ka lebaka la naetrojene e ngata, kahoo matla a eona a mochine ho feta mefuta e meng ea tšepe e sa hloekang ea austenitic e phahame. Ntle le moo, 254SMO e boetse e matla haholo ebile e na le tšusumetso e matla le ts'ebetso e ntle ea weldability.
4.254SMO e nang le molybdenum e phahameng e ka etsa hore e be tekanyo e phahameng ea oxidation ka annealing , eo ka mor'a hore acid e hloekisoe ka holim'a metsi a maholo ho feta tšepe e sa hloekang e tloaelehileng e tloaelehileng ho feta holim'a metsi. Leha ho le joalo, ha e e-s'o ame hampe ka lebaka la ho hanyetsa kutu ea tšepe ena.

 

Sebopeho sa metallurgic
254SMO ke sebopeho sa li-cubic lattice se bohareng ba sefahleho. E le hore u fumane sebopeho sa austenitic, 254SMO kakaretso annealing ho 1150-1200℃.Maemong a mang, thepa e ka 'na ea e-ba le mesaletsa ea karolo ea tšepe e bohareng (χ phase le α-phase). Leha ho le joalo, matla a bona a tšusumetso le khanyetso ea kutu ha e amehe hampe maemong a tloaelehileng. Ha li behiloe ka har'a 600-1000 ℃, li ka 'na tsa kena moeling oa lipula tsa lijo-thollo.

 

Khanyetso ea kutu
254SMO e nang le khabone e tlase haholo, ho bolelang hore kotsi ea ho futhumatsa e bakiloeng ke pula ea carbide e nyane haholo. Esita le ka 600-1000℃ ka mor'a hora sensitization ntse khona ho Strauss ka intergranular corrosion teko (Strauss Test ASTMA262 taelo E). Mokhahlelong o boletsoeng ka holimo oa mocheso oa intermetallic le monyetla oa ho ba le tšepe moeling oa lijo-thollo pula. sediments tsena u se ke ua etsa hore ho etsahala intergranular kutu ka likopo corrosion mecha ea phatlalatso, ka nako eo, tjheseletsa ka ho phethahatsoa ntle intergranular corrosion.Empa ka mocheso oa concentrated nitric acid, sediments tsena ka 'na etsa hore intergranular rusion ka libaka mocheso ameha. Haeba tšepe e tloaelehileng e sa hloekang ka har'a tharollo e nang le chloride, bromide kapa iodide, e tla bonts'a pitting, crevice corrosion kapa stress corrosion cracking form by localized corrosion. Leha ho le joalo, maemong a mang, ho ba teng ha halide ho tla potlakisa ho bola ha junifomo. Haholo-holo ka acid e non-oxidizing. Ka sulfuric acid e hloekileng, 254SMO e nang le khanyetso e kholo ea ho senya ho feta 316 (tšepe e tloaelehileng e sa hloekang), empa e na le khanyetso e fokotsehileng ea ho senya ha e bapisoa le 904L (NO8904) tšepe e sa hloekang haholo. Ka sulfuric acid e nang le li-ion tsa chloride, 254SMO e nang le matla a maholo ka ho fetisisa a ho thibela ho bola. The 316 e ke ke ea sebelisoa bakeng sa tšepe e sa hloekang ka hydrochloric acid kaha e ka 'na ea hlaha sebakeng sa corrosion le junifomo corrosion, empa 254SMO e ka sebelisoa ka diluted hydrochloric acid ka mocheso o tloaelehileng. , ka tlas'a moeli oa sebaka ha ho hlokahale hore u tšoenyehe ka ho bola ho etsahetse. Leha ho le joalo, re lokela ho leka ho qoba mapetsong a lekhalo. Ho silicate ea fluoride (H2SiF4) le hydrofluoric acid (HF), khanyetso ea kutu ea tšepe e tloaelehileng e sa tsitsang e fokola haholo, 'me 254SMO e ka sebelisoa mocheso o pharaletseng haholo le mahloriso.

 

Sebaka se sebelisitsoeng:
254SMO ke sesebelisoa se nang le merero e mengata se ka sebelisoang lits'ebetsong tse ngata tsa indasteri:
1. Petroleum, lisebelisoa tsa petrochemical, lisebelisoa tsa petro-chemical, joalo ka melumo.
2. Thepa le lisebelisoa tsa ho hloekisa pampiri, tse kang ho pheha pulp, bleaching, ho hlatsoa li-filters tse sebelisoang ka barrel le li-cylinder pressure rollers, joalo-joalo.
3. Thepa ea motlakase ea feme ea khase ea desulphurization, tšebeliso ea likarolo tse kholo: tora ea ho monya, flue le poleiti ea ho emisa, karolo e kahare, sistimi ea ho fafatsa.
4. Sets'oants'o sa ts'ebetso ea metsi a leoatleng kapa leoatleng, joalo ka lifeme tsa motlakase tse sebelisang metsi a leoatle ho pholisa Condenser e nang le marako a masesaane, ho tlosoa letsoai ka lisebelisoa tsa ho lokisa metsi a leoatle, ho ka sebelisoa le hoja metsi a ka 'na a se ke a phalla ka har'a sesebelisoa.
5. Liindasteri tsa ho ntša letsoai, tse kang lisebelisoa tsa letsoai kapa tsa ho ntša letsoai.
6. Mocheso oa mocheso, haholo-holo sebakeng se sebetsang sa ion chloride.