STAINLESS SUPER DUPLEX STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 GRAD F61 BI STRUTTURA B'ŻEWĠ FAŻI GĦALL-INDUSTRIJA KIMIKA SKOND EN 10088-1.
| Standard | Grad tal-Azzar | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Kompożizzjoni Kimika % | ||||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Lu: | Ni: | Cu: | N: | |
| EN | 1.4507 – X2CrNiMoCuN25-6-3 | |||||||||
| <0.03 | <2.0 | <0.7 | <0.035 | <0.015 | 24.0 – 26.0 | 3.0 – 4.0 | 6.0 – 8.0 | 1.0 – 2.5 | 0.20 – 0.30 | |
| ASTM | UNS S32550 – A182 grad F61 – Tip 255 | |||||||||
| <0.04 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 27.0 | 2.9 – 3.9 | 4.5 – 6.5 | 1.5 – 2.5 | 0.10 – 0.25 | |
| ASTM | UNS S32520 – A182 grad F59 | |||||||||
| <0.03 | <1.5 | <0.8 | <0.035 | <0.020 | 24.0 – 26.0 | 3.0 – 5.0 | 5.5 – 8.0 | 0.5 – 3.0 | 0.20 – 0.35 | |
| JIS | SUS329J4L – SUS 329J4L | |||||||||
| <0.03 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 26.0 | 2.5 – 3.5 | 5.5 – 7.5 | - | 0.08 – 0.30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, Grad F61 – speċifikazzjoni u applikazzjoni
Grad speċjali mill-grupp ta 'azzar li ma jissaddadx reżistenti għall-aċidu super-qawwi simili għal 1.4410 / X2CrNiMoN25-7-4 / UNS S32750. L-azzar juri proprjetajiet ta 'saħħa għolja b'reżistenza relattivament għolja għal diversi tipi ta' korrużjoni, inkluża korrużjoni intergranulari. Il-materjali 1.4507 u UNS S32550 jintużaw fl-industriji tal-karta, kimiċi, nitroġenu u tal-avjazzjoni kif ukoll fl-inġinerija tal-enerġija għal viti, xaftijiet, kmiem, fittings, installazzjonijiet u pipelines, partijiet tal-pompi, tankijiet għal kimiċi, skambjaturi tas-sħana, partijiet tar-radjaturi u kostruzzjonijiet ta' ajruplani.
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 - proprjetajiet mekkaniċi
- Saħħa tat-tensjoni, Rm: 700 – 900 MPa
- Il-punt ta' rendiment, Rp0,2: >500 MPa
- Titwil, A:> 25%
- Modulu ta 'elastiċità, E: 200 GPa
- Ebusija, HB: <270
- Kapaċità termali, cp: 500 J * kg-1 * K-1
- Konduttività termali, λ: 15 W * m-1 * K-1
- Koeffiċjent ta 'espansjoni lineari, α: 13.0 * 10-6 K-1
- Reżistenza speċifika, Ω: 0.8 mkOhm * m
Proprjetajiet mekkaniċi f'temperatura elevata - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Temperatura (℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Koeffiċjent ta' espansjoni lineari, α (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Modulu ta' elastiċità, E (GPa) | 194 | - | 186 | - | 180 | |||
| Il-punt ta' rendiment, Rp0,2 (MPa) | >450 | >420 | >400 | > 380 | - | |||
Trattament tas-sħana u tal-plastik 1.4507, UNS S32550
- Supersaturazzjoni f'1020 – 1100 ℃
- Irrumblar u forġa f'temperatura ta '1200 – 900 ℃