STAINLESS SUPER DUPLEX STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 GRADE F61 ME TE WHANGA-RUA MO TE AUHITUHI MAU KI TE EN 10088-1.
| Paerewa | Koeke maitai | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Hanga matū % | ||||||||||
| C: | Mn: | Ko: | P: | S: | Kr: | Mo: | Ko: | Cu: | N: | |
| EN | 1.4507 – X2CrNiMoCuN25-6-3 | |||||||||
| <0.03 | <2.0 | <0.7 | <0.035 | <0.015 | 24.0 – 26.0 | 3.0 – 4.0 | 6.0 – 8.0 | 1.0 – 2.5 | 0.20 – 0.30 | |
| ASTM | UNS S32550 – A182 kōeke F61 – Momo 255 | |||||||||
| <0.04 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 27.0 | 2.9 – 3.9 | 4.5 – 6.5 | 1.5 – 2.5 | 0.10 – 0.25 | |
| ASTM | UNS S32520 – A182 kōeke F59 | |||||||||
| <0.03 | <1.5 | <0.8 | <0.035 | <0.020 | 24.0 – 26.0 | 3.0 – 5.0 | 5.5 – 8.0 | 0.5 – 3.0 | 0.20 – 0.35 | |
| JIS | SUS329J4L – SUS 329J4L | |||||||||
| <0.03 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 26.0 | 2.5 – 3.5 | 5.5 – 7.5 | - | 0.08 – 0.30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, Kōeke F61 – te whakatakotoranga me te tono
Koeke motuhake mai i te roopu o nga tira kowiri tira-a-waikawa tino kaha e rite ana ki te 1.4410 / X2CrNiMoN25-7-4 / UNS S32750. Ko te maitai e whakaatu ana i nga ahuatanga kaha me te kaha o te aukati ki nga momo waikura, tae atu ki te waikura intergranular. Ko nga rauemi 1.4507 me UNS S32550 e whakamahia ana i roto i te pepa, te matū, te hauota, me nga umanga rererangi tae atu ki te miihini hiko mo nga miihini, nga kakau, nga ringaringa, nga taputapu, nga whakaurunga me nga paipa, nga waahanga papu, nga taika mo nga matū, nga whakawhiti wera, nga waahanga radiator me hanga rererangi.
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 – āhuatanga miihini
- Te kaha tensile, Rm: 700 – 900 MPa
- Te ira tuku, Rp0,2: >500 MPa
- Whakaroa, A:> 25%
- Modulus of elasticity, E: 200 GPa
- Pakeke, HB: <270
- Te kaha o te wera, cp: 500 J * kg-1 * K-1
- Te kawe werawera, λ: 15 W * m-1 * K-1
- Te whakarea roha raina, α: 13.0 * 10-6 K-1
- Atete motuhake, Ω: 0.8 mkOhm * m
Nga taonga miihini i te teitei teitei - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Te pāmahana (℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Te whakarea roha raina, α (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Kōwae o te elasticity, E (GPa) | 194 | - | 186 | - | 180 | |||
| Te ira tuku, Rp0,2 (MPa) | >450 | >420 | >400 | >380 | - | |||
Te wera me te maimoatanga kirihou 1.4507, UNS S32550
- Supersaturation i te 1020 – 1100 ℃
- Te hurihuri me te maaka i te mahana o te 1200 – 900 ℃
Wā tuku: Maehe-23-2020