STAINLESS SUPER DUPLEX STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 GRADE F61 MISY STRUCTURE ROA FAHAGAGANA HO AN'NY INDUSTRI CHEMIKA ARAKA NY EN 10088-1.
| Malagasy | Grade vy | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Famoronana simika% | ||||||||||
| C: | Mn: | Sy: | P: | S: | Cr: | Mo: | Ni: | Cu: | N: | |
| EN | 1.4507 – X2CrNiMoCuN25-6-3 | |||||||||
| <0.03 | <2.0 | <0.7 | <0.035 | <0,015 | 24.0 – 26.0 | 3.0 – 4.0 | 6.0 – 8.0 | 1.0 – 2.5 | 0.20 – 0.30 | |
| ASTM | UNS S32550 - A182 kilasy F61 - karazana 255 | |||||||||
| <0.04 | <1.5 | <1.0 | <0,040 | <0,030 | 24.0 – 27.0 | 2.9 – 3.9 | 4.5 – 6.5 | 1.5 – 2.5 | 0.10 – 0.25 | |
| ASTM | UNS S32520 - A182 kilasy F59 | |||||||||
| <0.03 | <1.5 | <0.8 | <0.035 | <0,020 | 24.0 – 26.0 | 3.0 – 5.0 | 5.5 – 8.0 | 0.5 – 3.0 | 0.20 – 0.35 | |
| JIS | SUS329J4L - SUS 329J4L | |||||||||
| <0.03 | <1.5 | <1.0 | <0,040 | <0,030 | 24.0 – 26.0 | 2.5 – 3.5 | 5.5 – 7.5 | - | 0.08 – 0.30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, Grade F61 - famaritana sy fampiharana
Kilasy manokana avy amin'ny vondron'ireo vy tsy misy asidra mahatohitra asidra mahery vaika mitovy amin'ny 1.4410 / X2CrNiMoN25-7-4 / UNS S32750. Ny vy dia mampiseho toetra matanjaka amin'ny fanoherana avo lenta amin'ny karazana harafesina isan-karazany, anisan'izany ny harafesina intergranular. Ny fitaovana 1.4507 sy UNS S32550 dia ampiasaina amin'ny indostrian'ny taratasy, simika, azota ary fiaramanidina ary koa amin'ny injeniera herinaratra ho an'ny screws, shafts, sleeves, fittings, installations and pipelines, pump parts, tank for chemicals, heat exchangers, radiator parts and fanorenana fiaramanidina .
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 - toetra mekanika
- Herin'ny tensile, Rm: 700 – 900 MPa
- Ny teboka vokatra, Rp0,2: >500 MPa
- Elongation, A:> 25%
- Modulus ny elasticité, E: 200 GPa
- Harness, HB: <270
- Fahafahana mafana, cp: 500 J * kg-1 * K-1
- Conductivity mafana, λ: 15 W * m-1 * K-1
- Lisitra fanitarana coefficient, α: 13.0 * 10-6 K-1
- fanoherana manokana, Ω: 0.8 mkOhm * m
Toetra mekanika amin'ny hafanana avo - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Temperature (℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Lisitra fanitarana coefficient, α (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Modulus ny elasticité, E (GPa) | 194 | - | 186 | - | 180 | |||
| Ny vokatra azo, Rp0,2 (MPa) | >450 | >420 | >400 | >380 | - | |||
Fitsaboana hafanana sy plastika 1.4507, UNS S32550
- Supersaturation amin'ny 1020 - 1100 ℃
- Rolling sy forging amin'ny mari-pana 1200 - 900 ℃