Ditunjuk minangka UNS N08825 utawa DIN W.Nr. 2.4858, Incoloy 825 (uga dikenal minangka "Alloy 825") minangka paduan wesi-nikel-kromium kanthi tambahan molybdenum, cooper lan titanium. Tambahan molybdenum nambah resistance kanggo pitting korosi ing aplikasi karat banyu nalika isi tembaga bestows resistance kanggo asam sulfat. Titanium ditambahake kanggo stabilisasi. Alloy 825 nduweni resistensi sing apik banget kanggo nyuda lan ngoksidasi asam, kanggo retak karat stres, lan serangan lokal kayata korosi pitting lan crevice. Utamane tahan kanggo asam sulfat lan fosfat. Campuran Incoloy 825 utamane digunakake kanggo pangolahan kimia, pipa petrokimia, peralatan kontrol polusi, pipa sumur minyak lan gas, pangolahan ulang bahan bakar nuklir, produksi asam, lan peralatan pickling.
1. Syarat Komposisi Kimia
| Komposisi Kimia Incoloy 825,% | |
|---|---|
| nikel | 38.0-46.0 |
| wesi | ≥22.0 |
| Kromium | 19.5-23.5 |
| Molybdenum | 2.5-3.5 |
| Tembaga | 1.5-3.0 |
| titanium | 0.6-1.2 |
| Karbon | ≤0.05 |
| Mangan | ≤1.00 |
| belerang | ≤0,030 |
| silikon | ≤0,50 |
| alumunium | ≤0.20 |
2. Sifat Mekanik Incoloy 825
Incoloy 825 weld gulu flanges 600# SCH80, diprodhuksi kanggo ASTM B564.
| Kekuwatan Tarik, min. | Kekuwatan Ngasilake, min. | Elongation, min. | Modulus elastik | |||
|---|---|---|---|---|---|---|
| Mpa | ksi | Mpa | ksi | % | Gpa | 106psi |
| 690 | 100 | 310 | 45 | 45 | 206 | 29.8 |
3. Sipat Fisik Incoloy 825
| Kapadhetan | Lebur Range | Panas Spesifik | Resistivitas listrik | ||
|---|---|---|---|---|---|
| g/cm3 | °C | °F | J/kg.k | Btu/lb. °F | µΩ·m |
| 8.14 | 1370-1400 | 2500-2550 | 440 | 0.105 | 1130 |
4. Wangun Produk lan Standar Incoloy 825
| wangun produk | Standar |
|---|---|
| Rod lan bar | ASTM B425, DIN17752 |
| Piring, sheet lan strips | ASTM B906, B424 |
| Pipa lan tabung sing mulus | ASTM B423, B829 |
| Pipa sing dilas | ASTM B705, B775 |
| Tabung sing dilas | ASTM B704, B751 |
| Fitting pipa sing dilas | ASTM A366 |
| Forging | ASTM B564, DIN17754 |
Wektu kirim: Oct-23-2020