BABBAN SUPER DUPLEX STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 GRADE F61 TARE DA SIFFOFIN TSARI BIYU DON SANA'AR CHEMICAL GAME DA EN 10088-1.
| Daidaitawa | Karfe daraja | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Haɗin Sinadari% | ||||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Mo: | Ni: | Ku: | N: | |
| EN | 1.4507 - X2CrNiMoCuN25-6-3 | |||||||||
| <0.03 | <2.0 | <0.7 | <0.035 | <0.015 | 24.0 - 26.0 | 3.0 - 4.0 | 6.0 - 8.0 | 1.0 - 2.5 | 0.20 - 0.30 | |
| ASTM | UNS S32550 - A182 daraja F61 - Nau'in 255 | |||||||||
| <0.04 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 - 27.0 | 2.9 - 3.9 | 4.5 - 6.5 | 1.5-2.5 | 0.10 - 0.25 | |
| ASTM | UNS S32520 - A182 digiri F59 | |||||||||
| <0.03 | <1.5 | <0.8 | <0.035 | <0.020 | 24.0 - 26.0 | 3.0 - 5.0 | 5.5 - 8.0 | 0.5 - 3.0 | 0.20 - 0.35 | |
| JIS | SUS329J4L - SUS 329J4L | |||||||||
| <0.03 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 - 26.0 | 2.5 - 3.5 | 5.5-7.5 | - | 0.08 - 0.30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, Grade F61 - ƙayyadaddun bayanai da aikace-aikace
Darajoji na musamman daga rukuni na bakin ƙarfe mai ƙarfi mai ƙarfi acid mai kama da 1.4410 / X2CrNiMoN25-7-4 / UNS S32750. Ƙarfe yana ba da babban kaddarorin ƙarfi tare da juriya mai girma ga nau'ikan lalata iri-iri, gami da lalatawar intergranular. 1.4507 da UNS S32550 kayan ana amfani da su a cikin takarda, sunadarai, nitrogen, da masana'antun jiragen sama da kuma injiniyoyin wutar lantarki don sukurori, shafts, hannayen riga, kayan aiki, shigarwa da bututun, sassan famfo, tankuna don sinadarai, masu musayar zafi, sassan radiator da gine-ginen jirgin sama .
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 - kayan inji
- Ƙarfin juzu'i, Rm: 700 - 900 MPa
- Matsakaicin yawan amfanin ƙasa, Rp0,2:>500 MPa
- Tsawaitawa, A:> 25%
- Modulus na elasticity, E: 200 GPa
- Taurin, HB: <270
- Ƙarfin zafi, cp: 500 J * kg-1 * K-1
- Ƙarfin wutar lantarki, λ: 15 W * m-1 * K-1
- Ƙididdigar faɗaɗa madaidaiciyar layi, α: 13.0 * 10-6 K-1
- Takamaiman juriya, Ω: 0.8 mkOhm * m
Kaddarorin injina a yanayin zafi mai girma - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Zazzabi (℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Ƙididdigar faɗaɗa layin layi, α (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Modulus na elasticity, E (GPa) | 194 | - | 186 | - | 180 | |||
| Matsakaicin yawan amfanin ƙasa, Rp0,2 (MPa) | >450 | >420 | >400 | >380 | - | |||
Maganin zafi da filastik 1.4507, UNS S32550
- Supersaturation a 1020 - 1100 ℃
- Juyawa da ƙirƙira a zazzabi na 1200 - 900 ℃
Lokacin aikawa: Maris 23-2020