Alloy C-4 Sinadarin takin:

Alloy	%	Ni	Cr	Mo	Fe	C	Mn	Si	Co	S	P	Ti
C-4	Min.	65	14	14
Max.		18	17	3.0	0.01	1.0	0.08	2.0	0.010	0.025	0.70

 

Yawan yawa	8.64 g/cm 3
Wurin narkewa	1350-1400 ℃

 

Alloy	Ƙarfin ƙarfi N/mm2	Ƙarfin bayarwa RP0.2N/mm2	Tsawaitawa A5%
C-4	783	365	55

Alloy C-4 alloy ne nickel-chromium-molybdenum gami da fice
high-zazzabi kwanciyar hankali kamar yadda shaida ta high ductility da lalata juriya ko da
bayan tsufa a cikin kewayon 1200 zuwa 1900 F (649 zuwa 1038 C). Wannan gami yana tsayayya da samuwar
na hatsi-iyaka precipitates a weld zafi yankin da ya shafa, don haka sa shi dace
don mafi yawan aikace-aikacen aiwatar da sinadarai a cikin yanayin as-welded. C-4 kuma
yana da kyakkyawan juriya ga fashewar damuwa-lalata da yanayin iskar oxygen har zuwa
1900F (1038 C).

 

Alloy C-4 alloy yana da na musamman juriya ga m iri-iri sinadaran tsari
yanayi. Wadannan sun hada da zafi gurbataccen ma'adinai acid, kaushi, chlorine
da chlorine gurbataccen kafofin watsa labarai (kwayoyin halitta da inorganic), busassun chlorine, formic da
acetic acid, acetic anhydride, da ruwan teku da brine mafita.
Alloy C-4 alloy za a iya ƙirƙira, zafi-bacin rai, da kuma tasiri extruded. Ko da yake
gami yana son yin aiki da ƙarfi, ana iya samun nasarar zana shi, zurfafa, latsa kafa ko
naushi. Duk hanyoyin da ake amfani da su na walda za a iya amfani da su don walda Alloy C-4
gami, ko da yake oxy-acetylene da submerged arc matakai ba a ba da shawarar
lokacin da aka yi nufin abin da aka ƙirƙira don amfani a cikin sabis na lalata. Kariya ta musamman
ya kamata a ɗauka don guje wa shigar da zafi mai yawa.