STEEL Super DUPLEX stainless X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 ìre F61 le STRUCHD-OBRACH dà-ìre airson gnìomhachas ceimigeach a rèir EN 10088-1.
| Inbhe | Ìre stàilinn | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| co-dhèanamh ceimigeach % | ||||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Mo: | Ni: | cu: | N: | |
| EN | 1.4507 - X2CrNiMoCuN25-6-3 | |||||||||
| <0.03 | <2.0 | <0.7 | <0.035 | <0.015 | 24.0 – 26.0 | 3.0 – 4.0 | 6.0 – 8.0 | 1.0-2.5 | 0.20 – 0.30 | |
| ASTM | UNS S32550 - A182 ìre F61 - Seòrsa 255 | |||||||||
| <0.04 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 27.0 | 2.9-3.9 | 4.5-6.5 | 1.5-2.5 | 0.10 - 0.25 | |
| ASTM | UNS S32520 - A182 ìre F59 | |||||||||
| <0.03 | <1.5 | <0.8 | <0.035 | <0.020 | 24.0 – 26.0 | 3.0 – 5.0 | 5.5 – 8.0 | 0.5 – 3.0 | 0.20 - 0.35 | |
| JIS | SUS329J4L – SUS 329J4L | |||||||||
| <0.03 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 26.0 | 2.5-3.5 | 5.5-7.5 | - | 0.08 – 0.30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, Ìre F61 - sònrachadh agus iarrtas
Ìre sònraichte bhon bhuidheann de steels stainless fìor-làidir searbhagach coltach ri 1.4410 / X2CrNiMoN25-7-4 / UNS S32750. Tha feartan àrd-neart aig an stàilinn le neart an aghaidh diofar sheòrsaichean de chreachadh, a’ gabhail a-steach corran eadar-roinneil. Tha stuthan 1.4507 agus UNS S32550 air an cleachdadh anns na gnìomhachasan pàipeir, ceimigeach, naitrigean, agus itealain a bharrachd air ann an innleadaireachd cumhachd airson sgriothan, shailean, sleeves, criathran, ionadan agus pìoban, pàirtean pumpaidh, tancaichean airson ceimigean, luchd-iomlaid teas, pàirtean radiator agus togail itealain.
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 - feartan meacanaigeach
- Neart tensile, Rm: 700 - 900 MPa
- An ìre toraidh, Rp0,2:> 500 MPa
- Leudachadh, A:> 25%
- Modal elasticity, E: 200 GPa
- cruas, HB: <270
- Comas teirmeach, cp: 500 J * kg-1 * K-1
- Thermal conductivity, λ: 15 W * m-1 * K-1
- Co-èifeachd leudachaidh sreathach, α: 13.0 * 10-6 K-1
- Frithealadh sònraichte, Ω: 0,8 mkOhm * m
Feartan meacanaigeach aig teòthachd àrdaichte - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Teòthachd ( ℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Co-èifeachd leudachaidh sreathach, α (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Modal elasticity, E (GPa) | 194 | - | 186 | - | 180 | |||
| An ìre toraidh, Rp0,2 (MPa) | >450 | > 420 | >400 | >380 | - | |||
Làimhseachadh teas is plastaig 1.4507, UNS S32550
- Supersaturation aig 1020 - 1100 ℃
- Rolladh agus cruthachadh aig teòthachd 1200 - 900 ℃