SUPER DUPLEX STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 GRÁD F61 LE STRUCHTÚR DÁ CHÉIM DON TIONSCAL CEIMICEACH DE RÉIR EN 10088-1.
| Caighdeán | Grád Cruach | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Comhdhéanamh Ceimiceach % | ||||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Mo: | Ni: | cu: | N: | |
| EN | 1.4507 – X2CrNiMoCuN25-6-3 | |||||||||
| <0.03 | <2.0 | <0.7 | <0.035 | <0.015 | 24.0 – 26.0 | 3.0 – 4.0 | 6.0 – 8.0 | 1.0 – 2.5 | 0.20 – 0.30 | |
| ASTM | UNS S32550 – A182 grád F61 – Cineál 255 | |||||||||
| <0.04 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 27.0 | 2.9 – 3.9 | 4.5 – 6.5 | 1.5 – 2.5 | 0.10 – 0.25 | |
| ASTM | UNS S32520 – A182 grád F59 | |||||||||
| <0.03 | <1.5 | <0.8 | <0.035 | <0.020 | 24.0 – 26.0 | 3.0 – 5.0 | 5.5 – 8.0 | 0.5 – 3.0 | 0.20 – 0.35 | |
| JIS | SUS329J4L – SUS 329J4L | |||||||||
| <0.03 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 26.0 | 2.5 – 3.5 | 5.5 – 7.5 | - | 0.08 – 0.30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, Grád F61 - sonraíocht agus cur i bhfeidhm
Grád speisialta ón ngrúpa de steels dhosmálta sár-láidir aigéad-resistant cosúil le 1.4410 / X2CrNiMoN25-7-4 / UNS S32750. Léiríonn an cruach airíonna ard-neart le friotaíocht réasúnta ard ar chineálacha éagsúla creimeadh, lena n-áirítear creimeadh intergranular. Úsáidtear ábhair 1.4507 agus UNS S32550 sna tionscail páipéir, ceimiceacha, nítrigine agus eitlíochta chomh maith le hinnealtóireacht chumhachta le haghaidh scriúnna, seaftaí, sleeves, feistis, suiteálacha agus píblínte, páirteanna caidéil, umair le haghaidh ceimiceán, malartóirí teasa, páirteanna radaitheora agus tógálacha aerárthaí .
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 – airíonna meicniúla
- Neart teanntachta, Rm: 700 - 900 MPa
- An pointe toraidh, Rp0,2:> 500 MPa
- Fadú, A:> 25%
- Modal elasticity, E: 200 GPa
- Cruas, HB: <270
- Cumas teirmeach, cp: 500 J * kg-1 * K-1
- Seoltacht theirmeach, λ: 15 W * m-1 * K-1
- Comhéifeacht leathnú líneach, α: 13.0 * 10-6 K-1
- Friotaíocht shonrach, Ω: 0.8 mkOhm * m
Airíonna meicniúla ag teocht ardaithe - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Teocht (℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Comhéifeacht leathnú líneach, α (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Modal leaisteachas, E (GPa) | 194 | - | 186 | - | 180 | |||
| An pointe toraidh, Rp0,2 (MPa) | >450 | > 420 | >400 | >380 | - | |||
Cóireáil teasa agus plaisteach 1.4507, UNS S32550
- Supersaturation ag 1020 - 1100 ℃
- Rollta agus brionnú ag teocht 1200 - 900 ℃
Am postála: Mar-23-2020