STAINLESS SUPER DUPLEX STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 GRADE F61 MEI TWEE-FASE STRUKTUR FOAR CHEMISCHE INDUSTRY NEVEN EN 10088-1.
| Standert | Steel Grade | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Gemyske gearstalling % | ||||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Mo: | Ni: | Cu: | N: | |
| EN | 1.4507 - X2CrNiMoCuN25-6-3 | |||||||||
| <0.03 | <2.0 | <0.7 | <0.035 | <0.015 | 24.0 – 26.0 | 3.0 – 4.0 | 6,0 – 8,0 | 1.0 – 2.5 | 0.20 - 0.30 | |
| ASTM | UNS S32550 - A182 klasse F61 - Type 255 | |||||||||
| <0.04 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 27.0 | 2.9 – 3.9 | 4,5 – 6,5 | 1,5 – 2,5 | 0,10 – 0,25 | |
| ASTM | UNS S32520 - A182 klasse F59 | |||||||||
| <0.03 | <1.5 | <0.8 | <0.035 | <0.020 | 24.0 – 26.0 | 3.0 – 5.0 | 5,5 – 8,0 | 0,5 – 3,0 | 0,20 - 0,35 | |
| JIS | SUS329J4L - SUS 329J4L | |||||||||
| <0.03 | <1.5 | <1.0 | <0.040 | <0.030 | 24.0 – 26.0 | 2,5 – 3,5 | 5,5 – 7,5 | - | 0.08 – 0.30 | |
1.4507, X2CrNiMoCuN25-6-3, UNS S32550, Grade F61 - spesifikaasje en tapassing
Spesjale klasse út de groep fan super-sterk soere-resistant RVS stielen fergelykber mei 1.4410 / X2CrNiMoN25-7-4 / UNS S32750. It stiel hat hege sterkte eigenskippen mei relatyf hege wjerstân tsjin ferskate soarten korrosysje, ynklusyf yntergranulêre korrosje. 1.4507- en UNS S32550-materialen wurde brûkt yn 'e papier-, gemyske, stikstof- en loftfeartyndustry, lykas yn' e machttechnyk foar skroeven, assen, mouwen, fittings, ynstallaasjes en pipelines, pompdielen, tanks foar gemikaliën, waarmtewikselers, radiatordielen en fleanmasines konstruksjes.
1.4507, X2CrNiMoCuN25-6-3, UNS S32550 - meganyske eigenskippen
- Treksterkte, Rm: 700 – 900 MPa
- It opbringstpunt, Rp0,2: >500 MPa
- Elongation, A:> 25%
- Elasticiteitsmodulus, E: 200 GPa
- Hardheid, HB: <270
- Termyske kapasiteit, cp: 500 J * kg-1 * K-1
- Termyske conductivity, λ: 15 W * m-1 * K-1
- Lineêre útwreidingskoëffisjint, α: 13,0 * 10-6 K-1
- Spesifike wjerstân, Ω: 0,8 mkOhm * m
Meganyske eigenskippen by ferhege temperatuer - 1.4507, X2CrNiMoCuN25-6-3, UNS S32550
| Temperatuer (℃) | 100 | 150 | 200 | 250 | 300 | |||
|---|---|---|---|---|---|---|---|---|
| Lineêre útwreidingskoëffisjint, α (* 10-6 K-1) | 13.0 | - | 13.5 | - | 14.0 | |||
| Elastisiteitsmodulus, E (GPa) | 194 | - | 186 | - | 180 | |||
| It opbringstpunt, Rp0,2 (MPa) | >450 | >420 | >400 | >380 | - | |||
Warmte- en plestikbehanneling 1.4507, UNS S32550
- Supersaturation by 1020 - 1100 ℃
- Rôlje en smeden by in temperatuer fan 1200 - 900 ℃