STAINLESS SUPER DUPLEX STEEL X2CRNIMOCUN25-6-3, 1.4507, UNS S32550, A182 GRADE F61 WITH TWO-PHASE STRUCTURE FOR CHEMICAL INDUSTRY ACCORDING TO EN 10088-1.

የማይዝግ ሱፐር ዱፕሌክስ ብረት X2CRNIMOCUN25-6-3፣ 1.4507፣ UNS S32550፣ A182 ግሬድ F61 ባለሁለት-ደረጃ መዋቅር ለኬሚካል ኢንዱስትሪ በEN 10088-1 መሠረት።

መደበኛ	የአረብ ብረት ደረጃ
	የኬሚካል ቅንብር %
	C:	ሚ፡	ሲ፡	P:	S:	ክ.	ሞ፡	ናይ፡	ኩ፡	N:
EN	1.4507 - X2CrNiMoCuN25-6-3
EN	<0.03	<2.0	<0.7	<0.035	<0.015	24.0 - 26.0	3.0 - 4.0	6.0 - 8.0	1.0 - 2.5	0.20 - 0.30
ASTM	UNS S32550 - A182 ክፍል F61 - ዓይነት 255
ASTM	<0.04	<1.5	<1.0	<0.040	<0.030	24.0 - 27.0	2.9 - 3.9	4.5 - 6.5	1.5 - 2.5	0.10 - 0.25
ASTM	UNS S32520 - A182 ክፍል F59
ASTM	<0.03	<1.5	<0.8	<0.035	<0.020	24.0 - 26.0	3.0 - 5.0	5.5 - 8.0	0.5 - 3.0	0.20 - 0.35
JIS	SUS329J4L - SUS 329J4L
JIS	<0.03	<1.5	<1.0	<0.040	<0.030	24.0 - 26.0	2.5 - 3.5	5.5 - 7.5	-	0.08 - 0.30

1.4507፣ X2CrNiMoCuN25-6-3፣ UNS S32550፣ ክፍል F61 - መግለጫ እና መተግበሪያ

ከ1.4410/X2CrNiMoN25-7-4/UNS S32750 ጋር የሚመሳሰሉ እጅግ በጣም ጠንካራ አሲድ-የሚቋቋሙ አይዝጌ ብረቶች ቡድን ልዩ ደረጃ። አረብ ብረት ኢንተርግራንላር ዝገትን ጨምሮ ለተለያዩ የዝገት ዓይነቶች በአንጻራዊነት ከፍተኛ የመቋቋም ችሎታ ያላቸውን ከፍተኛ ጥንካሬ ባህሪያትን ያሳያል። 1.4507 እና UNS S32550 ቁሳቁሶች በወረቀት, በኬሚካል, በናይትሮጅን እና በአቪዬሽን ኢንዱስትሪዎች እንዲሁም በሃይል ኢንጂነሪንግ ውስጥ ለዊልስ, ዘንጎች, እጅጌዎች, መለዋወጫዎች, ተከላዎች እና የቧንቧ መስመሮች, የፓምፕ ክፍሎች, የኬሚካል ታንኮች, የሙቀት መለዋወጫዎች, የራዲያተሩ ክፍሎች እና የአውሮፕላን ግንባታዎች .

1.4507፣ X2CrNiMoCuN25-6-3፣ UNS S32550 - ሜካኒካል ባህርያት

የመጠን ጥንካሬ, Rm: 700 - 900 MPa
የምርት ነጥብ፣ Rp0፣2:>500 MPa
ማራዘም፣ A:> 25%
የመለጠጥ ሞጁል, ኢ: 200 ጂፒኤ
ጠንካራነት፣ HB፡ <270
የሙቀት አቅም, cp: 500 J * kg-1 * K-1
የሙቀት መቆጣጠሪያ, λ: 15 W * m-1 * K-1
መስመራዊ የማስፋፊያ ቅንጅት፣ α: 13.0 * 10-6 K-1
የተወሰነ መቋቋም, Ω: 0.8 mkOhm * m

ሜካኒካል ባህርያት ከፍ ባለ የሙቀት መጠን - 1.4507፣ X2CrNiMoCuN25-6-3፣ UNS S32550

የሙቀት መጠን (℃)	100	150	200	250	300
መስመራዊ የማስፋፊያ ቅንጅት፣ α (* 10-6 K-1)	13.0	-	13.5	-	14.0
የመለጠጥ ሞጁል፣ ኢ (ጂፒኤ)	194	-	186	-	180
የምርት ነጥብ፣ Rp0,2 (MPa)	> 450	> 420	> 400	> 380	-

የሙቀት እና የፕላስቲክ ህክምና 1.4507, UNS S32550

በ 1020 - 1100 ℃ ላይ ከፍተኛ ሙሌት
በ 1200 - 900 ℃ የሙቀት መጠን ማሽከርከር እና መፈጠር